| 1. Identificação | ||||
| Tipo de Referência | Artigo em Revista Científica (Journal Article) | |||
| Site | mtc-m21b.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34P/3QLL2K8 | |||
| Repositório | sid.inpe.br/mtc-m21b/2018/03.05.12.19 (acesso restrito) | |||
| Última Atualização | 2018:03.05.12.19.40 (UTC) administrator | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21b/2018/03.05.12.19.40 | |||
| Última Atualização dos Metadados | 2019:01.14.17.05.24 (UTC) administrator | |||
| DOI | 10.1088/2053-1591/aaa467 | |||
| ISSN | 2053-1591 | |||
| Chave de Citação | OliveiraGuOiHeCoReBo:2018:CaNaOb | |||
| Título | Carbon nanofibers obtained from electrospinning process  | |||
| Ano | 2018 | |||
| Mês | Feb. | |||
| Data de Acesso | 17 maio 2024 | |||
| Tipo de Trabalho | journal article | |||
| Tipo Secundário | PRE PI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 1516 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Oliveira, Juliana Bovi de 2 Guerrini, Lília Müller 3 Oishi, Silvia Sizuka 4 Hein, Luis Rogerio de Oliveira 5 Conejo, Luíza dos Santos 6 Rezende, Mirabel Cerqueira 7 Botelho, Edson Cocchieri | |||
| ORCID | 1 0000-0003-2460-2930 2 3 0000-0001-5540-3382 4 5 0000-0001-5533-1374 | |||
| Grupo | 1 2 3 LABAS-COCTE-INPE-MCTIC-GOV-BR | |||
| Afiliação | 1 Universidade Estadual Paulista (UNESP) 2 Universidade Federal de São Paulo (UNIFESP) 3 Instituto Nacional de Pesquisas Espaciais (INPE) 4 Universidade Estadual Paulista (UNESP) 5 Universidade Estadual Paulista (UNESP) 6 Universidade Federal de São Paulo (UNIFESP) 7 Universidade Estadual Paulista (UNESP) | |||
| Endereço de e-Mail do Autor | 1 2 3 silvia.oishi@inpe.br | |||
| Revista | Materials Research Express | |||
| Volume | 5 | |||
| Número | 2 | |||
| Páginas | e025602 | |||
| Histórico (UTC) | 2018-03-05 12:22:11 :: simone -> administrator :: 2018 2019-01-14 17:05:24 :: administrator -> simone :: 2018 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Tipo de Versão | publisher | |||
| Palavras-Chave | polyacrylonitrile electrospinning carbon nanofibers carbonization | |||
| Resumo | In recent years, reinforcements consisting of carbon nanostructures, such as carbon nanotubes, fullerenes, graphenes, and carbon nanofibers have received significant attention due mainly to their chemical inertness and good mechanical, electrical and thermal properties. Since carbon nanofibers comprise a continuous reinforcing with high specific surface area, associated with the fact that they can be obtained at a low cost and in a large amount, they have shown to be advantageous compared to traditional carbon nanotubes. The main objective of this work is the processing of carbon nanofibers, using polyacrylonitrile (PAN) as a precursor, obtained by the electrospinning process via polymer solution, with subsequent use for airspace applications as reinforcement in polymer composites. In this work, firstly PAN nanofibers were produced by electrospinning with diameters in the range of (375 +/- 85) nm, using a dimethylformamide solution. Using a furnace, the PAN nanofiber was converted into carbon nanofiber. Morphologies and structures of PAN and carbon nanofibers were investigated by scanning electron microscopy, Raman Spectroscopy, thermogravimetric analyses and differential scanning calorimeter. The resulting residual weight after carbonization was approximately 38% in weight, with a diameters reduction of 50%, and the same showed a carbon yield of 25%. From the analysis of the crystalline structure of the carbonized material, it was found that the material presented a disordered structure. | |||
| Área | FISMAT | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção anterior à 2021 > LABAS > Carbon nanofibers obtained... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Idioma | en | |||
| Arquivo Alvo | oliveira_carbon.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/3ESR3H2 | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2013/09.24.19.30 5 | |||
| Divulgação | WEBSCI; PORTALCAPES; SCOPUS. | |||
| Acervo Hospedeiro | sid.inpe.br/mtc-m21b/2013/09.26.14.25.20 | |||
| 6. Notas | ||||
| Campos Vazios | alternatejournal archivingpolicy archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes parameterlist parentrepositories previousedition previouslowerunit progress project resumeid rightsholder schedulinginformation secondarydate secondarykey secondarymark session shorttitle sponsor subject tertiarymark tertiarytype url | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||